00 CAMPUS ARISTÓTELES CALAZANS SIMÕES (CAMPUS A. C. SIMÕES) CTEC - CENTRO DE TECNOLOGIA TRABALHOS DE CONCLUSÃO DE CURSO (TCC) - GRADUAÇÃO - CTEC Trabalhos de Conclusão de Curso (TCC) - Graduação - ENGENHARIA QUÍMICA - CTEC
Use este identificador para citar ou linkar para este item: http://www.repositorio.ufal.br/jspui/handle/riufal/7621
Tipo: Trabalho de Conclusão de Curso
Título: Síntese da zeólita ZSM-12 com baixas concentrações de direcionadores orgânicos, na presença de N-Butilamina
Título(s) alternativo(s): Synthesis of zeolite ZSM-12 with low concentrations of organic directing, in the presence of N-Butylamine
Autor(es): Sampaio, Danillo Alcides dos Santos
Primeiro Orientador: Alencar, Soraya Lira
metadata.dc.contributor.advisor-co1: Solano, Julyane da Rocha Santos
metadata.dc.contributor.referee1: Urbina, Maritza Montoya
metadata.dc.contributor.referee2: Silva, Albanise Enide da
Resumo: O presente trabalho visou encontrar uma rota de síntese mais econômica e viável para a zeólita ZSM-12, uma vez que, a utilização de agentes orgânicos direcionadores de estrutura (OSDA’s) são geralmente evitados em sínteses de zeólitas comerciais devido a fatores econômicos e ambientais. As sínteses foram realizadas por meio do método hidrotérmico, combinando n-butilamina com reduzidas concentrações dos direcionadores de estrutura cloreto de metiltrietilamônio (MTEACl) e brometo de tetraetilamônio (TEABr). Para a obtenção dos materiais sintetizados, adotaram-se os seguintes parâmetros para o gel de síntese: razão molar SiO2/Al2O3 = 100; razão molar direcionador/SiO2 = 0,15 e 0,20; razão molar n-butilamina/SiO2 = 0,20 e 0,30; temperatura de 170oC e tempos de cristalização entre 12 e 144 horas. As amostras obtidas foram caracterizadas por difratometria de raios-X (DRX), análises termogravimétricas (TG/DTG) e adsorção de nitrogênio (pelo método BET). De acordo com os resultados obtidos, a melhor amostra da zeólita ZSM-12 foi a sintetizada utilizando o direcionador orgânico MTEACl, com razão molar MTEA+/SiO2 = 0,20, razão molar n-butilamina/SiO2 = 0,30 e tempo de cristalização de 72h.
Abstract: The present work aimed to find a more economical and viable synthesis route for zeolite ZSM-12, since the use of organic structure-directing agents (OSDA's) is generally avoided in commercial zeolites syntheses due to factors economic and environmental. The syntheses were performed using the hydrothermal method, combining n-butylamine with reduced concentrations of methyltriethylammonium chloride (MTEACl) and tetraethylammonium bromide (TEABr). To obtain the synthesized materials, the following parameters were adopted for the synthesis gel: SiO2/Al2O3 molar ratio = 100; molar ratio directing/SiO2 = 0.15 and 0.20; molar ratio n-butylamine/SiO2 = 0.20 and 0.30; temperature of 170oC and crystallization times between 12 and 144 hours. The samples obtained were characterized by X-ray diffractometry (XRD), thermogravimetric analysis (TG/DTG) and nitrogen adsorption (by the BET method). According to the results obtained, the best sample of ZSM-12 zeolite was synthesized using the organic driver MTEACl, with molar ratio MTEA+/SiO2 = 0.20, molar ratio n-butylamine/SiO2 = 0.30 and crystallization time of 72h.
Palavras-chave: Zeólita ZSM-12
N-Butilamina
Agente orgânico direcionador de estrutura
Cloreto de metiltrietilamônio
Brometo de tetraetilamônio
Zeolite ZSM-12
N-Butylamine
Organic structure-directing agent
Methyltriethylammonium chloride
Tetraethylammonium romide
CNPq: CNPQ::ENGENHARIAS::ENGENHARIA QUIMICA
Idioma: por
País: Brasil
Editor: Universidade Federal de Alagoas
Sigla da Instituição: UFAL
metadata.dc.publisher.department: Curso de Engenharia Química
Citação: SAMPAIO, Danillo Alcides dos Santos. Síntese da zeólita ZSM-12 com baixas concentrações de direcionadores orgânicos, na presença de N-Butilamina. 2019. 60 f. Trabalho de Conclusão de Curso (Bacharelado em Engenharia Química) - Centro de Tecnologia, Curso de Engenharia Química, Universidade Federal de Alagoas, Maceió, 2021.
Tipo de Acesso: Acesso Aberto
URI: http://www.repositorio.ufal.br/handle/riufal/7621
Data do documento: 5-nov-2019
Aparece nas coleções:Trabalhos de Conclusão de Curso (TCC) - Graduação - ENGENHARIA QUÍMICA - CTEC



Os itens no repositório estão protegidos por copyright, com todos os direitos reservados, salvo quando é indicado o contrário.