00 CAMPUS ARISTÓTELES CALAZANS SIMÕES (CAMPUS A. C. SIMÕES) CTEC - CENTRO DE TECNOLOGIA Dissertações e Teses defendidas na UFAL - CTEC
Use este identificador para citar ou linkar para este item: http://www.repositorio.ufal.br/jspui/handle/riufal/5551
Tipo: Tese
Título: Síntese da ZSM-5 de alto teor de sílica com sementes na presença de etanol e aminas
Autor(es): Mendonça, Thayane Regine Dantas de
Primeiro Orientador: Silva, Antonio Osimar Sousa da
metadata.dc.contributor.referee1: Galdino, Fabiane Caxico de Abreu
metadata.dc.contributor.referee2: Meili, Lucas
metadata.dc.contributor.referee3: Santos, Jailma Barros dos
metadata.dc.contributor.referee4: Souza, Felipe Thiago Caldeira de
Resumo: Neste estudo, foi avaliada a cristalização da ZSM-5 com razão Si/Al elevada (100 e 150) através do uso combinado de sementes de cristalização e adição de compostos orgânicos que não são direcionadores convencionais da ZSM-5 (etanol, metilamina, etilamina, propilamina, butilamina, isopropilamina e dietilamina), com intuito de estabelecer uma rota de síntese de menor impacto ambiental e baixo custo. Na etapa inicial, verificou-se o efeito do etanol e aminas adicionados ao gel de síntese, assim como, tempo de tratamento hidrotérmico e razões codirecionador/sílica e OH/sílica em condições de cristalização estáticas. Na segunda etapa, foi analisada a influência da agitação durante a cristalização sobre as propriedades da ZSM-5 obtida em condições otimizadas nos experimentos estáticos da etapa anterior. As zeólitas formadas foram analisadas por difratometria de raios X para compreender os efeitos dos tipos de direcionadores e demais parâmetros estudados sobre a formação desse material. Enquanto que, para as amostras mais cristalinas foram realizadas caracterizações adicionais por: dessorção de amônia à temperatura programada, adsorção de nitrogênio, microscopia eletrônica de varredura, espectroscopia de energia dispersiva de raios X e análises termogravimétricas. A partir desses dados, foi observado um decréscimo na cristalinidade devido a formação da fase contaminante magadiita com o aumento do tempo de síntese. Verificou que a fase magadiita é termicamente instável, desaparecendo após a etapa de calcinação a 550 ºC. Nas sínteses sob agitação, foram verificados compósitos de ZSM-5/magadiita/cristobalita, a fase cristobalita surgiu devido a tempos prolongados de tratamento hidrotérmico em conjunto com a agitação do sistema, sendo necessário, assim, ajustar os parâmetros de síntese para se estabelecer uma metodologia capaz de produzir a ZSM-5 com alta cristalinidade. Esse procedimento foi obtido com sucesso para a síntese da ZSM-5, utilizando propilamina como agente direcionador de estrutura alternativo, sob condições estáticas. O material formado por esse método exibiu um grau de cristalinidade superiore a amostra comercial padrão e tamanho médio de cristalito entre 23 e 24 nm. Sua área superficial específica foi superior a 300 m2.g-1 e o volume de microporos alcançou 0,09 cm3.g-1. A maior acessibilidade aos poros do catalisador com propilamina levaram a resultados catalíticos superiores em relação aos demais materiais avaliados, com baixa formação de coque, possuindo alta estabilidade no craqueamento do n-hexano.
Abstract: In this study, it was evaluated the crystallization of ZSM-5 with high Si/Al ratio (100 and 150) through combined use of crystallization seeds and addition of organic compounds which are not conventional templates of ZSM-5 (ethanol, methylamine, ethylamine, propylamine, butylamine, isopropylamine and diethylamine), intending to establish a route of synthesis with less environmental impact and low cost. In the first stage, it was verified the effect of ethanol and amines added to the synthesis gel, as well as the time of hydrothermal and ratios codirecting/silica and OH/silica in static crystallization conditions. In the second stage, it was analyzed the influence of agitation during the crystallization upon the ZSM-5’s proprieties obtained in optimized conditions on static experiments from the past stage. The zeolites formed were analyzed by X-ray diffractometry to comprehend the effects of template types and further studied parameters about this material’s formation, whilst for the most crystalline samples were realized additional characterizations for: desorption at the programmed temperature, nitrogen adsorption, scanning electronic microscopy, dispersive X-Ray energy spectroscopy and thermogravimetric analysis. Through these data, it was observed that the crystallinity decreased, due to the formation of the magadiite phase with increasement of the synthesis time. It was verified that the magadiite phase is thermally instable, disappearing after the stage of calcination at 550 °C. On synthesis under agitation, it was observed ZSM-5/magadiite/cristobalita composites. The cristobalite phase occurred due to prolonged times of hydrothermal treatment and the system agitation, making necessaire to adjust the synthesis parameters to establish a methodology able to produce the ZSM-5 with high crystallinity. This procedure was successfully obtained to the synthesis of ZSM-5, using propylamine as template agent of alternative structure, under static conditions. The material formed through this method showed a superior crystallinity rate over the standard commercial sample and average crystal size between 23 and 24 nm. Its superficial specific area was superior to 300 m2.g-1, and the microporous volume reached 0,09 cm3.g-1. The biggest accessibility to the catalyzer porous with propylamine led to superior catalytic results over further evaluated material, with low ratio of coke formation, showing high stability on n-hexane cracking.
Palavras-chave: ZSM-5 (Zeolitas)
Sílica
Aminas
Etanol
Microscopia eletrônica de varredura
Cristalização
Zeólitos sintéticos
ZSM-5 (Zeolites)
Amines
Ethanol
Scanning electron microscopy
Crystallization
Synthetic Zeolites
CNPq: CNPQ::ENGENHARIAS::ENGENHARIA DE MATERIAIS E METALURGICA
Idioma: por
País: Brasil
Editor: Universidade Federal de Alagoas
Sigla da Instituição: UFAL
metadata.dc.publisher.program: Programa de Pós-Graduação em Materiais
Citação: MENDONÇA, Thayane Regine Dantas de. Síntese da ZSM-5 de alto teor de sílica com sementes na presença de etanol e aminas. 2019. 93 f. Tese (Doutorado em Materiais) – Centro de Tecnologia, Programa de Pós-Graduação em Materiais, Universidade Federal de Alagoas, Maceió, 2019.
Tipo de Acesso: Acesso Aberto
URI: http://www.repositorio.ufal.br/handle/riufal/5551
Data do documento: 29-jan-2019
Aparece nas coleções:Dissertações e Teses defendidas na UFAL - CTEC

Arquivos associados a este item:
Arquivo Descrição TamanhoFormato 
Síntese da ZSM-5 de alto teor de sílica com sementes na presença de etanol e aminas.pdf3.32 MBAdobe PDFVisualizar/Abrir


Os itens no repositório estão protegidos por copyright, com todos os direitos reservados, salvo quando é indicado o contrário.