Tipo: | Tese |
Título: | Inibição de corrosão em concreto armado: eficiência e comportamento do sistema tiouréia/molibdato de sódio |
Título(s) alternativo(s): | Inhibition of corrosion in reinforced concrete: efficiency and behavior of the thiourea / sodium molybdate system |
Autor(es): | Uchôa, Silvia Beatriz Beger |
Primeiro Orientador: | Tonholo, Josealdo |
metadata.dc.contributor.referee1: | Scatena Júnior, Hélio |
metadata.dc.contributor.referee2: | Martinelli, Antônio Eduardo |
metadata.dc.contributor.referee3: | Paula, Francine Santos de |
metadata.dc.contributor.referee4: | Galdino, Fabiane Caxico de Abreu |
Resumo: | A corrosão de armaduras de concreto armado em pontes, viadutos e edifícios tem preocupado o meio técnico, pois além do custo de manutenção, há o custo indireto devido à quedas de estruturas, interdições e incômodos causados aos usuários. Entre os métodos para minimizar a corrosão, podem ser citados os inibidores de corrosão, os quais são adicionados ao concreto e atuam na interface concreto/aço, diminuindo a taxa de corrosão. Neste trabalho, são relatados os estudos do comportamento de inibidores de corrosão à base de molibdato de sódio e tiouréia, aplicados em concretos submetidos à ação de íons cloreto e comparados a dois inibidores comerciais. Foram realizados estudos em solução e em pastas, argamassas e concretos, com dois cimentos diferentes, sem e com adição de 5 e 10% de sílica ativa. A determinação das dosagens de inibidores foi feita em solução saturada de hidróxido de cálcio, utilizando técnicas eletroquímicas como polarização em estado quase-estacionário e voltametria cíclica. Foram estudados os efeitos dos inibidores propostos, em várias dosagens, e de dois inibidores comerciais, nas propriedades de pastas e concretos sem e com sílica ativa. Além da trabalhabilidade e da resistência à compressão, foi testada a resistência à penetração de cloretos pelos métodos ASTM C 1202 e ASTM C 1543. A avaliação da eficiência frente à corrosão provocada por íons cloreto seguiu a norma ASTM G 109. A resistividade elétrica foi determinada utilizando espectroscopia de impedância eletroquímica e condutivimetria. Os inibidores propostos, nas concentrações de 2% de molibdato de sódio e 0,67% de tiouréia, mostraram resultados bastante promissores, tanto na avaliação quanto à influência sobre as propriedades físicas e mecânicas do concreto, quanto à diminuição da penetração de cloretos e eficiência na inibição da corrosão. |
Abstract: | Rebar corrosion in reinforced concrete structures is a big issue to technical studies, because it has, besides the maintenance costs, indirect costs which affect bridges and building users. Corrosion inhibitors are chemical substances that added to concrete reduce or retard rebar corrosion. In this thesis we described the behavior of sodium molybdate and thiourea used as corrosion inhibitors (CI) for concrete mixes submitted to chloride medium. Calcium hydroxide solution, cement paste, mortar and concrete were used to understand corrosion inhibitors effects on their properties. Dosage study was performed using solutions, with and without the CI, applying cyclic voltammetry and steady-state polarization. Effects on cement paste and concrete were studied using four different dosages of the proposed CI and two commercial products, two different cements and silica fume as supplementary cementitious material. Concretes mixes were tested by workability, compression strength and resistance to chloride penetration, using ASTM C 1202 and ASTM C 1543. ASTM G 109 was used as standard to determine CI efficiency on corrosion inhibition and two techniques were used to determine concrete electrical resistivity: electrochemical impedance spectroscopy and conductivimetry. The proposed inhibitors showed, in 2% sodium molybdate and 0,67% thiourea, slight effects on concrete properties and good effects on improving the resistance to chloride penetration and to corrosion due chloride ions. |
Palavras-chave: | Concreto – Corrosão das armaduras Concreto armado – Durabilidade Inibidor de corrosão Concrete - Corrosion of reinforcement Reinforced Concrete - Durability Corrosion inhibitor |
CNPq: | CNPQ::CIENCIAS EXATAS E DA TERRA::QUIMICA::FISICO-QUIMICA::ELETROQUIMICA CNPQ::ENGENHARIAS::ENGENHARIA CIVIL::ESTRUTURAS::ESTRUTURAS DE CONCRETO |
Idioma: | por |
País: | Brasil |
Editor: | Universidade Federal de Alagoas |
Sigla da Instituição: | UFAL |
metadata.dc.publisher.program: | Programa de Pós-Graduação em Química e Biotecnologia |
Citação: | UCHÔA, Silvia Beatriz Beger. Inibição de corrosão em concreto armado: eficiência e comportamento do sistema tiouréia/molibdato de sódio. 2007. 219 f. Tese (Doutorado em Química e Biotecnologia) - Instituto de Química e Biotecnologia, Programa de Pós-Graduação em Química e Biotecnologia, Universidade Federal de Alagoas, Maceió, 2007. |
Tipo de Acesso: | Acesso Aberto |
URI: | http://www.repositorio.ufal.br/handle/riufal/2552 |
Data do documento: | 26-nov-2007 |
Aparece nas coleções: | Dissertações e Teses defendidas na UFAL - IQB |
Arquivos associados a este item:
Arquivo | Descrição | Tamanho | Formato | |
---|---|---|---|---|
Inibição de corrosão em concreto armado - eficiência e comportamento do sistema tiouréia-molibdato de sódio.pdf | Inibição de corrosão em concreto armado: eficiência e comportamento do sistema tiouréia/molibdato de sódio | 2.96 MB | Adobe PDF | Visualizar/Abrir |
Os itens no repositório estão protegidos por copyright, com todos os direitos reservados, salvo quando é indicado o contrário.